Made from BK7 material, which has transparent range from 330-2100nm. The refractive index is 1.5168 at 587.6nm. The BK7 window has good performance over visible and near IR spectrum for most application.
Achromatic Waveplate Achromatic Waveplates(Retarders), AWP is composed of one piece of Crystal Quartz and one piece of Magnesium Fluoride, MgF2.
Barium fluoride (BaF2) shows good optical transmission over UV-IR windows in 0.15μm~12.5μm.
MgF2 windows are used in the UV, visible and IR ranges, with approximately 94% transmission from 200 - 1000 nm, and approximately 95% transmission from 1-6µm
CaF2 has transparent range from 170-7800nm. The refractive index is 1.399 at 5000nm. 1. Low absorption coefficient 2. High damage threshold, 3. Low Dispersion (with an Abbe Number of 95) 4. Low fluorescence 5. Excellent water, chemical, and heat resistance
Optical Silver Coated Mirrors
Average Reflectance >90% from 400 nm to 20 µm
Shape could be customized: Round, Square, Elliptical, Right angle prisms
Material could be customized: Fused silica, Pyrex, N-BK7
product orgin:
Chinashipping port:
Fuzhou Chinapayment:
T/T Payment, Western UnionOptical Silver Coated Mirrors
Mirror is an object with a surface that has good specular reflection. that is, it is smooth enough to form an image. The most familiar type of mirror is the plane mirror, which has a flat surface. Curved mirror are also used, to produce magnified or demagnified images or focus light or simply distort the reflected image.
WTS make Silver Coated Mirrors, Gold Coated Mirrors, Aluminum Coated Mirrors, Dielectric Coated Mirrors.
The shape could be circle, square, elliptical or right angle prisms or glued together.
Typical Sizes:
Specifications:
Material:
N-BK7 ; UV Fused Silica ;other optical glass
Dimension Tolerance:
+0/-0.1mm
Thickness Tolerance:
'+/-0.1mm
Surface quality:
60/40
Clear Aperture:
>85%
Flatness:
λ/4 per 25mm@633nm
Parallelism:
<3'
Bevel:
<0.25mmx45°
Coating:
One surface(S1) :Polished and Metallic coating (Al, Ag, Au)
The other surface :Fine ground
Protected Aluminum :Ravg> 85%@400nm-800nm
VIS Enhanced Aluminum :Ravg> 90% @450nm-750nm
UV Enhanced Aluminum :Ravg > 80%@250nm-400nm
Protected Silver :Ravg > 90% @400nm-20um
Protected Gold :Ravg > 94% @650nm-16um
Size(mm)
Size(mm)
Φ5.0x1.0
10.0x10.0x3
Φ10.0x2.0
20.0x20.0x3
Φ12.7x2.0
25.4x25.4x3
Φ15.0x3.0
30.0x30.0x5
Optical Gold Coated Mirrors Average Reflectance >94% from 800 nm to 20 µm Shape could be customized: Round, Square, Elliptical, Right angle prisms Material could be customized: Fused silica, Pyrex, N-BK7
Optical Aluminum Coated Mirrors Average Reflectance >88% from 450 nm to 10 µm Shape could be customized: Round, Square, Elliptical, Right angle prisms Material could be customized: Fused silica, Pyrex, N-BK7
Rhomboid prisms are commonly used to displace a laser beam without changing its direction. Lateral Displacement of Beam Displaces Optical Axis Without Inverting Image
KTP crystal is mostly used as nonlinear crystals for frequency doubling of solid-state Nd:YAG crystal or Nd:YVO4 crystal laser, as it has large nonlinear optical coefficients, wide angular bandwidth and small walk-off angle, broad temperature and spectral bandwidth.
CaF2 has transparent range from 170-7800nm. The refractive index is 1.399 at 5000nm. 1. Low absorption coefficient 2. High damage threshold, 3. Low Dispersion (with an Abbe Number of 95) 4. Low fluorescence 5. Excellent water, chemical, and heat resistance
Right Angle Prism is deviating or deflecting a beam of light with 90°or 180°. It is often used in telescope, periscope and other optical system. Deviate Beam or Image by 90° or 180° Material: N-BK7, UV Fused Silica, CaF2, ZnSe, or Ge AR-Coated, HR coated are Available