Made from BK7 material, which has transparent range from 330-2100nm. The refractive index is 1.5168 at 587.6nm. The BK7 window has good performance over visible and near IR spectrum for most application.
Achromatic Waveplate Achromatic Waveplates(Retarders), AWP is composed of one piece of Crystal Quartz and one piece of Magnesium Fluoride, MgF2.
Barium fluoride (BaF2) shows good optical transmission over UV-IR windows in 0.15μm~12.5μm.
MgF2 windows are used in the UV, visible and IR ranges, with approximately 94% transmission from 200 - 1000 nm, and approximately 95% transmission from 1-6µm
CaF2 has transparent range from 170-7800nm. The refractive index is 1.399 at 5000nm. 1. Low absorption coefficient 2. High damage threshold, 3. Low Dispersion (with an Abbe Number of 95) 4. Low fluorescence 5. Excellent water, chemical, and heat resistance
MgF2 windows are used in the UV, visible and IR ranges, with approximately 94% transmission from 200 - 1000 nm, and approximately 95% transmission from 1-6µm
product orgin:
Chinashipping port:
Fuzhou Chinapayment:
T/T Payment, Western UnionIR Windows Magnesium Fluoride (MgF2) Windows
MgF2 has excellent transmission from deep in the ultraviolet region to the mid-infrared. MgF2 windows are extremely durable and introduce minimal aberrations. It is particularly useful for Excimer laser application.
MgF2 is one crystal with Orientation. WTS offer C-Axis and random Orientation MgF2 windows.
MgF2 Windows SPECIFICATION:
Material:
MgF2
Dimension Tolerance:
+0.0, -0.1mm
Thickness Tolerance:
± 0.1mm
Surface quality:
80/50
Clear Aperture:
>85%
Flatness:
λ per 25mm
Parallelism:
3'
Bevel:
<0.25mm X 45°
Coating:
Upon requirement
MgF2 Main Properties and Performance
Transmission range (μm)
0.11~7.5
Refractivity (0.7μm)
n0=1.37608 ne=1.38771
Reflection Loss at 0.6μm
5.2%(both faces)
Thermal expansion coefficient (℃-1)
13.7(//axis c), 8.9(⊥axis c)
Thermal conductivity at 300K (Wm-1K-1)
0.3
Knoop Hardness (kg/mm2)
415
Solubility (g/100gH2O·0℃)
0.0002
Density (g/cm3)
3.18
Melting Point (℃)
1255
|
Typical Sizes: |
|
| Round Shape | Φ5.0; Φ10.0 ; Φ12.7; Φ15.0; Φ20.0; |
| Diameter(mm): | Φ25.4; Φ30.0; Φ38.1; Φ50.8; Φ76.2 |
| Square Shape: | 5.0x5.0 ; 10.0x10.0 ; 15.0x15.0 ; |
| WxH(mm) | 20.0x20.0; 25.0x25.0; 50.0x50.0 |
| Thickness(mm): | 0.5; 1.0; 1.5; 2.0; 3.0; |
| 4.0; 5.0; 6.0; 8.0; 10.0 |
N-BK7 Windows and H-K9L Windows
Made from BK7 material, which has transparent range from 330-2100nm. The refractive index is 1.5168 at 587.6nm. The BK7 window has good performance over visible and near IR spectrum for most application.
Cut-Off Colored Glass Filters
Cut-off Colored Glass Filters The glass is named based on spectral characteristic of which is represented by the wavelength transmission limit. Short Pass Color Glass Filters Long Pass Color Glass filters
High Accuracy Corner Cube Prism
Retroreflectors (Corner Cube Prisms) reflect an image or beam back toward its original direction via three total internal reflections (TIR) 180° Reflection Inverts Image 3 arcsec Beam Deviation
High Accuracy Coated Hollow Retroreflectors
Hollow Retroreflectors are constructed of three first-surface mirrors assembled by a proprietary process into a mutually-orthogonal inside corner. Incident Light is Reflected Back to the Source Hollow Lightweight Design
IR Windows Zinc Sulfide ZnS Windows
ZnS is used widely for IR components, windows and lenses, and applied for Thermal Imaging, long-wave infrared sensors.
KTP Nonlinear Crystals
KTP crystal is mostly used as nonlinear crystals for frequency doubling of solid-state Nd:YAG crystal or Nd:YVO4 crystal laser, as it has large nonlinear optical coefficients, wide angular bandwidth and small walk-off angle, broad temperature and spectral bandwidth.
copyright © 2019 WTS PHOTONICS CO., LTD.all rights reserved. powered by dyyseo.com .
wts photonics
+86-591-83626970
sales@wts-photonics.com
markwts886
+86-15659898031
Follow us from facebook
Follow us from linkedin